DuPont Teijin Films Melinex® 313 Polyester Film
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 313 Polyester Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melinex® 313 is a general purpose polyester film with consistently good handling properties. It is pretreated on one side for adhesion.Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 100 MPa | 14500 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 100 MPa | 14500 psi | ASTM D882A |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882A |
| Film Elongation at Break, TD | 110 % | 110 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.5 % @Temperature 190 °C, Time 300 sec |
3.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 3.5 % @Temperature 190 °C, Time 300 sec |
3.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.6 % @Thickness 0.0122 mm |
3.6 % @Thickness 0.000480 in |
ASTM D1003 |
| 5.3 % @Thickness 0.0234 mm |
5.3 % @Thickness 0.000920 in |
ASTM D1003 | |
| Transmission, Visible | 87 % @Thickness 0.0234 mm |
87 % @Thickness 0.000920 in |
TLT; ASTM D1003 |
| 88.5 % @Thickness 0.0122 mm |
88.5 % @Thickness 0.000480 in |
TLT; ASTM D1003 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-LUBE 4220 Electrically Conductive Grease
- Lanxess Durethan® DP AKV 30 X HR EF 900116 Nylon 66, 30% Glass Fiber
- Silon Tabond 2006 Adhesive Resin
- SMAC CABLE® 2521S-60-08 Damping Material
- Shinkong Synthetic Fibers Shinite® N602 Nylon 66
- Cossa Polimeri ESTAPROP H 2560 C Polypropylene, 30% Mineral Filled
- ChevronTexaco HDAX® SAE 30 Low Ash Gas Engine Oil
- ExxonMobil PP5032E3 Polypropylene Copolymer
- Beijing Evergrow Resources Carbon Fiber Tissue
- Axiall 1701 Clear 7002 Flexible PVC
Copyright © lookpolymers.com All Rights Reserved