DuPont Teijin Films Mylar® MC2 Polyester Film, 50 Gauge (14 µm), PVDC Coated

Category Polymer , Film , Thermoplastic , Polyester, TP , PVDC , Polyvinyl Dichloride (PVDC) Coated Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® MC2 Polyester Film, 50 Gauge (14 µm), PVDC Coated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.A polyester film with a vacuum deposited layer of aluminum on one side and overcoated on both sides with a heat sealable PVDC copolymer. The film has excellent oxygen, moisture, and light barrier properties. It is available in 50 and 100 gauge. Can be used in plain and structured form to package snacks, candy, nuts, pharmaceuticals, dry chemicals, and other materials that require protection from moisture, oxygen, and light.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Average value for Mylar® films.
Moisture Vapor Transmission 0.00800 cc-mm/m²-24hr-atm
0.0203 cc-mil/100 in²-24hr-atm
ASTM E96 Procedure E
Water Vapor Transmission 0.600 g/m²/day
0.0386 g/100 in²/day
ASTM E96 Procedure E
Oxygen Transmission 0.00210 cc-mm/m²-24hr-atm
0.00533 cc-mil/100 in²-24hr-atm
or 0.15 cc/m²-24hr-atm for the film. ASTM D3985
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 100 %
100 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Modulus of Elasticity 3.45 GPa
500 ksi
(stiffness), ASTM D882
Tear Strength Test 300
300
Graves, g; ASTM D1004
Seal Strength 201 g/25 mm
201 g/in
Film Tensile Strength at Break, MD 165 MPa
23900 psi
ASTM D882
Film Tensile Strength at Break, TD 193 MPa
28000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Not cleared by FDA for food temperatures above this temperature.
Shrinkage 1.5 %

@Temperature 150 °C,
Time 1800 sec
1.5 %

@Temperature 302 °F,
Time 0.500 hour
Film shrinkage in oven.