DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and frozen foods. Mylar® OL12 is dual ovenable film which provides strong, aggressive seals to polar substrates such as amorphous polyester (APET, also PETG), semicrystalline polyester (CPET), polyester coated paperboard, and polyvinylchloride (PVC). Mylar® OL12 does not seal to polyethylene, polypropylene, or polystyrene. DuPont Teijin Films offers another family of lidding films (RL types) for sealing to these substrates. Mylar® OL12 has higher hot tack and a thicker seal layer than either Mylar® OL or OL2, and can be used in hot fill applications. It is not recommended for applications requiring retort sterilization. Mylar® OL12 lidding films have excellent grease and oil resistance. Heat seals produced with Mylar® OL12 are stronger than with Mylar® OL2 (or OL) and may be difficult to peel without shredding.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Calculated from nominal thickness and yield
Moisture Vapor Transmission 0.570 cc-mm/m²-24hr-atm
1.45 cc-mil/100 in²-24hr-atm
Proc. E; ASTM E96
Oxygen Transmission 1.89 cc-mm/m²-24hr-atm
4.80 cc-mil/100 in²-24hr-atm
Tested per ASTM D3985 at 22°C
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Secant Modulus 3.79 GPa
550 ksi
Stiffness Modulus; ASTM D882
Tear Strength Test 1.3
1.3
lb Graves; ASTM D1004
Film Tensile Strength at Break, MD 172 MPa
24900 psi
ASTM D882
Film Tensile Strength at Break, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
399 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F