DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 500 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Teijin® Tetoron®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 500 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Teijin® Tetoron® U2 is an opaque white polyester film. Teijin® Tetoron® U2 is available in the following variants:U2: Non-pretreated; available in 150, 200, 300, 400, 500 & 1000 gaugeU298W: Adhesion Pretreated (both sides); available in 750 & 1000 gaugeU2L98W: Low Shrinkage, Adhesion Pretreated (both sides); available in 500 gaugeTypical Applications: Prepaid cards (Magnetic Cards)LabelImagingInformation provided by DuPont.
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882A
130 %
130 %
U2L98W; ASTM D882A
Film Elongation at Break, TD 90 %
90 %
ASTM D882A
90 %
90 %
U2L98W; ASTM D882A
Film Tensile Strength at Break, MD 146.96 MPa
21315 psi
U2L98W; ASTM D882A
166.96 MPa
24215 psi
ASTM D882A
Film Tensile Strength at Break, TD 186.0 MPa
26970 psi
ASTM D882A
186.0 MPa
26970 psi
U2L98W; ASTM D882A
Thermal Properties Metric English Comments
Shrinkage, MD 0.30 %

@Temperature 150 °C,
Time 1800 sec
0.30 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained, U2L98W
1.0 %

@Temperature 150 °C,
Time 1800 sec
1.0 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Shrinkage, TD 0.00 %

@Temperature 150 °C,
Time 1800 sec
0.00 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained, U2L98W
0.10 %

@Temperature 150 °C,
Time 1800 sec
0.10 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Optical Properties Metric English Comments
Gloss 47 %
47 %
60°, U2L98W; ASTM D1003
48 %
48 %
60°; ASTM D1003
Descriptive Properties Value Comments
Color 0.1
a
0.1
a, U2L98W
-2.5
b
-2.5
b, U2L98W
91.6
L
92
L, U2L98W