E-Polymers SEPAZ® K365GM 60% Glass Fiber/Calcium Carbonate Reinforced General Purpose PPS Resin

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® K365GM 60% Glass Fiber/Calcium Carbonate Reinforced General Purpose PPS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidity leads to good dimensional precision. SEPAZ PPS applications: switches, connectors and other electronic and electric components, alternators and other automobile components, and office equipment components including chassis parts and housings.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.96 g/cc
1.96 g/cc
ASTM D792
Water Absorption 0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength 131.5 MPa
19070 psi
ASTM D638
Elongation at Break 1.0 %
1.0 %
ASTM D638
Flexural Strength 189.33 MPa
27460 psi
ASTM D790
Flexural Modulus 18.84 GPa
2732 ksi
ASTM D790
Izod Impact, Notched 0.422 J/cm
0.790 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Thickness 1.60 mm
10.0 µin/in-°F

@Thickness 0.0630 in
ASTM D696
CTE, linear, Transverse to Flow 31.0 µm/m-°C

@Thickness 1.60 mm
17.2 µin/in-°F

@Thickness 0.0630 in
ASTM D696
Melting Point 280 °C
536 °F
ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 266 °C
511 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
4.1

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 0.450 kV/mm

@Thickness 1.60 mm
11.4 kV/in

@Thickness 0.0630 in
ASTM D149
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 300 - 330 °C
572 - 626 °F
Mold Temperature 130 - 160 °C
266 - 320 °F
Drying Temperature 140 °C
284 °F
Dry Time 6 hour
6 hour