EMS-Grivory Grivory® BK-50 PA6-GB50
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BK-50 PA6-GB50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 |
| 95.0 MPa | 13800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 8.0 % | 8.0 % | dry; ISO 527-1/-2 |
| 25 % | 25 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.70 GPa | 247 ksi | conditioned; ISO 527-1/-2 |
| 6.10 GPa | 885 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | dry; ISO 179/1eU |
| 3.50 J/cm² @Temperature 30.0 °C |
16.7 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA |
| 0.400 J/cm² | 1.90 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 80.0 - 110 °C | 176 - 230 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | conditioned; IEC 60243-1 |
| 36.0 kV/mm | 914 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 450 V | 450 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Electricals & Electronics | Electrical appliances | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NH9338 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- Reltek BONDiT™ B-4682 Adhesive and Sealant
- Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber
- Lucas-Milhaupt Lucanex 616 Active Metal Brazing
- Techmer ES HiFill® PA6 0201 B Barium Sulfate Filler
- Total LDPE LA 0710 Low Density Polyethylene - Extrusion Coating
- Clariant Renol PPSP0017 Polypropylene, Static Dissipative
- Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion
- Arlon R37908R015L Silicone Rubber/Fiberglass/Acrylic/Polyester
Copyright © lookpolymers.com All Rights Reserved