EMS-Grivory Grivory® L 20A Z PA12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® L 20A Z PA12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Grilamid L 20A Z is a medium viscosity product, based on Polyamide 12 (PA12). Grilamid L 20A Z is impact modified, hydrolysis-and heat stabilized. Grilamid L 20A Z is used for production of high valued injection molding parts, and extrusion blow molding parts. The special features of Grilamid L 20A Z are: Hydrolysis- and heat stabilityImpact resistance at low temperatures Good chemical resistance Good resistance to oil High surface quality Good dimensional stability High processing speed Low density, low weightApplication examples: Grilamid L 20A Z is suitable for injection molding parts and extrusion blow molding parts in automotive applications.Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
ISO 1183
Water Absorption 1.5 %
1.5 %
ISO 62
Moisture Absorption 0.700 %
0.700 %
ISO 62
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
conditioned, 15s; ISO 868
Tensile Strength at Break 45.0 MPa
6530 psi
conditioned; ISO 527-1/-2
Tensile Strength, Yield 30.0 MPa
4350 psi
dry; ISO 527-1/-2
40.0 MPa
5800 psi
dry; ISO 527-1/-2
Elongation at Break 45 %
45 %
conditioned; ISO 527-1/-2
Elongation at Yield 10 %
10 %
conditioned; ISO 527-1/-2
15 %
15 %
dry; ISO 527-1/-2
Tensile Modulus 0.900 GPa
131 ksi
conditioned; ISO 527-1/-2
1.20 GPa
174 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched NB
NB
dry; ISO 179/1eU
NB
NB
conditioned; ISO 179/1eU
NB

@Temperature 30.0 °C
NB

@Temperature 86.0 °F
dry; ISO 179/1eU
NB

@Temperature 30.0 °C
NB

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 7.00 J/cm²
33.3 ft-lb/in²
conditioned; ISO 179/1eA
1.50 J/cm²

@Temperature 30.0 °C
7.14 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 140 µm/m-°C
77.8 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 90.0 - 110 °C
194 - 230 °F
long term; EMS
150 °C
302 °F
short term; EMS
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 45.0 °C
113 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
conditioned; IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 28.0 kV/mm
711 kV/in
conditioned; IEC 60243-1
Comparative Tracking Index 600 V
600 V
conditioned; IEC 60112
Descriptive Properties Value Comments
Automotive Fuel systems
Electricals & Electronics Cables & Tubes
Form Granules
Industry & Consumer goods Hydraulics & Pneumatics
Sports & Leisure
Tools & Accessories
Processing Other Extrusion
Special Characteristics High impact or impact modified
Improved heat resistance
Improved UV resistance (outdoor use)