EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Grivory XE 4217 black 9233 is a high heat stabilized, 45% glass fiber reinforced, semicrystalline, thermoplastic engineering material for injection moulding. Polymer designation according to ISO: PA 6T/66+X Acc. to ASTM: PPA, polyphthalamide. The main distinguishing feature of Grivory HT-PPA, when compared to other polyamides, is its good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. The special property profile of Grivory XE 4217 black 9233 makes it suitable for automotive parts with very high demands on heat stability. Parts of good surface quality are feasible. Grivory XE 4217 black 9233 is applicable for engine compartment and power-train applications such as:Charge air ductsCharge air cooler tanksAir intake silencersOil sumpsFunctional partsInformation provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption 4.3 %
4.3 %
ISO 62
Moisture Absorption 1.70 %
1.70 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 250 MPa
36300 psi
conditioned; ISO 2039-1
270 MPa
39200 psi
dry; ISO 2039-1
Tensile Strength at Break 165 MPa
23900 psi
conditioned; ISO 527-1/-2
230 MPa
33400 psi
dry; ISO 527-1/-2
Elongation at Break 2.7 %
2.7 %
dry; ISO 527-1/-2
2.7 %
2.7 %
conditioned; ISO 527-1/-2
Tensile Modulus 13.0 GPa
1890 ksi
conditioned; ISO 527-1/-2
15.0 GPa
2180 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
dry; ISO 179/1eU
8.00 J/cm²
38.1 ft-lb/in²
conditioned; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
dry; ISO 179/1eA
1.10 J/cm²
5.23 ft-lb/in²
conditioned; ISO 179/1eA
0.900 J/cm²

@Temperature 30.0 °C
4.28 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
0.900 J/cm²

@Temperature 30.0 °C
4.28 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-1/-2
Melting Point 300 °C
572 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 150 °C
302 °F
long term; EMS
250 °C
482 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
dry; IEC 60093
1.00e+12 ohm-cm
1.00e+12 ohm-cm
conditioned; IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 45.0 kV/mm
1140 kV/in
dry; IEC 60243-1
45.0 kV/mm
1140 kV/in
conditioned; IEC 60243-1
Comparative Tracking Index 600 V
600 V
conditioned; IEC 60112
Descriptive Properties Value Comments
Automotive Air intake sytems
Fuel systems
Hydraulic systems
Interior
Powertrain and Chassis
Electricals & Electronics Electrical equipment
Form Granules
Industry & Consumer goods Hydraulics & Pneumatics
Mechanical Engineering
Power transmission
Tools & Accessories
Processing Injection Molding
Product Attributes Bio based Polyamide
Co Polyamide
Improved alcohol resistance
Partially aromatic Polyamide
Special Characteristics Improved heat resistance