Eastman E6838-899F Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman E6838-899F Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
E6838-899F is a low density formulation with no slip or antiblock. It is suggested for film applications requiring high clarity, good tear and impact strength, a wide heat-sealing range, and good printability. Common end uses include convertor film for food and industrial packaging. Users must make their own determination of its safety, lawfulness, and technical suitability in their intended applications.Unless otherwise noted, all tests are run at 23°C and 50% RH. Extrusion conditions used to produce 1.25 mil blown film: 1.9:1 blow-up ratio.Applications:Converter film for foodFood packagingFood-contact applicationsIndustrial packagingE6838-899F is a low density formulation with no slip or antiblock. It is suggested for film applications requiring high clarity, good tear and impact strength, a wide heat-sealing range, and good printability. Common end uses include convertor film for food and industrial packaging. As supplied by Eastman Chemical, E6838-899F may lawfully be used in food-contact applications under the FDA regulations at 21 CFR 177.1520(c)(2.2). Users must make their own determination of its safety, lawfulness, and technical suitability in their intended applications.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D4883
Moisture Vapor Transmission 19.0 cc-mm/m²-24hr-atm
48.3 cc-mil/100 in²-24hr-atm
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D1434
Thickness 31.8 microns
1.25 mil
Melt Flow 1.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 28.0 MPa
4060 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 380 %
380 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.172 GPa
24.9 ksi
1% Secant; ASTM D882
Secant Modulus, TD 0.193 GPa
28.0 ksi
1% Secant; ASTM D882
Coefficient of Friction >= 1.0
>= 1.0
ASTM D1894
Elmendorf Tear Strength MD 320 g
320 g
Elmendorf Tear Strength TD 150 g
150 g
Elmendorf Tear Strength, MD 10.1 g/micron
257 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.70 g/micron
119 g/mil
ASTM D1922
Dart Drop 2.70 g/micron
68.6 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 28.0 MPa
4060 psi
ASTM D882
Film Tensile Strength at Break, TD 21.0 MPa
3050 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.5 %
4.5 %
ASTM D1003
Gloss 70 %
70 %
at 45°; ASTM D2457
Transmission, Visible 55 %
55 %
ASTM D1746
Descriptive Properties Value Comments
Process Film