Eastman Tenite 105-23 Cellulose Acetate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 105-23 Cellulose Acetate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 3.3 % | 3.3 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.62 J/cm² | 7.71 ft-lb/in² | |
| 0.590 J/cm² @Temperature -30.0 °C |
2.81 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 101 µm/m-°C @Temperature 20.0 °C |
56.1 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 129 µm/m-°C @Temperature 20.0 °C |
71.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 87.0 °C | 189 °F | |
| Glass Transition Temp, Tg | 106 °C | 223 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 245 °C | 446 - 473 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® A 5000 AE Expandable Polystyrene, Standard Flame Retardant
- SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific)
- DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d
- SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East)
- Tisan TISLAMID® 66 30% Glass Bead Reinforced Nylon 66
- Elastocon TPE Technologies Elastocon® 2825 Thermoplastic Elastomer
- 3M 9628FL Double Coated Tape with Quick Bonding Adhesive 360
- Resinlab® EP1121 Black Electronic Grade Epoxy Encapsulant
- BASF Ultradur® B 4300 G3 High Speed 15% Glass Filled BK 15045 PBT
Copyright © lookpolymers.com All Rights Reserved