Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer Eastman Chemical
Trade Name Tenite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:Blood TherapyDrug DeliveryIV ComponentsMedical DevicesSurgical InstrumentsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenitecellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite Cellulose Acetate Propionate 350-13 has a plasticizer level of 13%. It meets FDA requirements for certain food-contact applications when supplied in specific FDA color numbers.Information provided by Eastman.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 1.5 %

@Time 86400 sec
1.5 %

@Time 24.0 hour
Immersion; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 85
85
ASTM D785
Tensile Strength at Break 38.3 MPa
5550 psi
ASTM D638
Tensile Strength, Yield 34.5 MPa
5000 psi
ASTM D638
Elongation at Break 40 %
40 %
ASTM D638
Flexural Strength 44.9 MPa
6510 psi
ASTM D790
Flexural Modulus 1.586 GPa
230.0 ksi
ASTM D790
Izod Impact, Notched 1.02 J/cm

@Temperature -40.0 °C
1.91 ft-lb/in

@Temperature -40.0 °F
ASTM D256
3.21 J/cm

@Temperature 23.0 °C
6.01 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 110 - 170 µm/m-°C
61.1 - 94.4 µin/in-°F
ASTM D696
Specific Heat Capacity 1.26 - 1.67 J/g-°C
0.301 - 0.399 BTU/lb-°F
DSC
Thermal Conductivity 0.170 - 0.330 W/m-K
1.18 - 2.29 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C
187 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
ASTM D648
Vicat Softening Point 103 °C
217 °F
ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.46 - 1.49
1.46 - 1.49
n<sub>D</sub>; ASTM D542
Haze <= 8.5 %
<= 8.5 %
ASTM D1003
Transmission, Visible >= 90 %
>= 90 %
ASTM E308
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 - 1.00e+15 ohm-cm
1.00e+13 - 1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.3 - 3.8

@Frequency 1.00e+6 Hz
3.3 - 3.8

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 11.8 - 18.7 kV/mm
300 - 475 kV/in
ASTM D149
Dissipation Factor 0.010 - 0.15

@Frequency 1.00e+6 Hz
0.010 - 0.15

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Formula Number 350
Plasticizer 13 percent
Soluble Matter Loss 0.1 percent
ASTM D570
Weight Loss on Heating 0.6 percent
ASTM D707, 72 hrs, 80°C