Elektro-Isola G-Etronax EP 203 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler
Manufacturer Elektro-Isola
Trade Name G-Etronax
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Elektro-Isola G-Etronax EP 203 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: High mechanical strength at elevated temperatures. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. Can be used at cryogenic temperatures. Very good resistance to chemicals.Information provided by Elektro-Isola
Physical Properties Metric English Comments
Density 1.85 g/cc
0.0668 lb/in³
24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption 0.20 %
0.20 %
24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2
Mechanical Properties Metric English Comments
Tensile Strength 320 MPa

@Thickness >=1.50 mm
46400 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity 22.0 GPa

@Thickness >=1.50 mm
3190 ksi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength 280 MPa

@Thickness >=1.50 mm
40600 psi

@Thickness >=0.0591 in
1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1
450 MPa

@Thickness >=1.50 mm
65300 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Compressive Strength 550 MPa

@Thickness >=5.00 mm
79800 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength 50.0 MPa

@Thickness >=5.00 mm
7250 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO) 65.0 kJ/m²

@Thickness >=5.00 mm
30.9 ft-lb/in²

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 160 °C

@Thickness 0.000 mm,
Time 7.20e+7 sec
320 °F

@Thickness 0.000 in,
Time 20000 hour
IEC 60216; IEC/EN 60893-2 7.1
Electrical Properties Metric English Comments
Insulation Resistance 5.00e+11 ohm

@Thickness >=3.00 mm
5.00e+11 ohm

@Thickness >=0.118 in
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant 4.5

@Thickness <=3.00 mm,
Frequency 50.0 Hz
4.5

@Thickness <=0.118 in,
Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
4.5

@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz
4.5

@Thickness <=0.118 in,
Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength 2.40 kV/mm

@Thickness >=3.00 mm
61.0 kV/in

@Thickness >=0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
16.0 kV/mm

@Thickness 3.00 mm
406 kV/in

@Thickness 0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor 0.0080

@Frequency 50.0 Hz
0.0080

@Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index 200 V

@Thickness 3.00 mm
200 V

@Thickness 0.118 in
IEC 60112; IEC/EN 60893-2 6.4