Epoxy Technology EPO-TEK® 360T High Temperature Epoxy

Category	Polymer , Thermoset , Epoxy , Epoxy, High Temperature
Manufacturer	Epoxy Technology
Trade Name	EPO-TEK®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Epoxy Technology EPO-TEK® 360T High Temperature Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Material Description: A two component, high-temperature grade, electrically and thermally insulating epoxy for semiconductor, electronics, fiber optics and medical applications. It is a thixotropic paste for non-flow properties.Information Provided by Epoxy Technology

Physical Properties	Metric	English	Comments
Specific Gravity	1.02 g/cc	1.02 g/cc	Part B
	1.16 g/cc	1.16 g/cc	Part A
Particle Size	<= 20 µm	<= 20 µm
Viscosity	4000 - 6000 cP @Temperature 23.0 °C	4000 - 6000 cP @Temperature 73.4 °F	50 rpm

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	75	75
Tensile Modulus	2.19 GPa	318 ksi	Storage
Shear Strength	13.77 MPa	1997 psi	Lap
	>= 23.4 MPa	>= 3400 psi	Die

Thermal Properties	Metric	English	Comments
CTE, linear	53.0 µm/m-°C	29.4 µin/in-°F	Below Tg
	146 µm/m-°C	81.1 µin/in-°F	Above Tg
Maximum Service Temperature, Air	175 °C	347 °F	Continuous
	275 °C	527 °F	Intermittent
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F	Continuous
	-55.0 °C	-67.0 °F	Intermittent
Glass Transition Temp, Tg	>= 80.0 °C	>= 176 °F	Dynamic Cure 20—200°C /ISO 25 Min; Ramp 10—200°C @ 20°C/Min
Decomposition Temperature	341 °C	646 °F	Degradation Temperature

Electrical Properties	Metric	English
Volume Resistivity	<= 2.00e+13 ohm-cm	<= 2.00e+13 ohm-cm
Dielectric Constant	3.84 @Frequency 1000 Hz	3.84 @Frequency 1000 Hz
Dissipation Factor	0.014 @Frequency 1000 Hz	0.014 @Frequency 1000 Hz

Processing Properties	Metric	English	Comments
Cure Time	1.00 min @Temperature 150 °C	0.0167 hour @Temperature 302 °F	minimum
	10.0 min @Temperature 100 °C	0.167 hour @Temperature 212 °F	minimum
Pot Life	240 min	240 min
Shelf Life	6.00 Month @Temperature 25.0 °C	6.00 Month @Temperature 77.0 °F

Descriptive Properties	Value	Comments
Color	Amber	Part B
	Tan	Part A
Consistency	Thixotropic paste
Mix Ratio By Weight	100:10
Number of Components	Two
Thixotropic Index	5.1
Weight Loss	0.59%	200°C
	1.79%	250°C
	4.26%	300°C