- Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide ACF2 is a 10% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 230 MPa | 33400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | ROA; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Quadrant EPP Fluorosint® MT-01 Proprietary fluoropolymer reinforced with carbon fibers and organometallic fillers( ASTM Product Data Sheet)
- Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized
- Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F)
- SK Chemicals SKYTHANE® S175A Polyester Based Thermoplastic Polyurethane Elastomer
- Hexcel® HexTow™ IM9 Carbon Fiber
- Axiall CL-7049 Rigid PVC, Molding
- Asahi Kasei Xyron® 240Z Modified Polyphenylene Ether
- Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved