Eurostar Staramide AG4K PA66, 20% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Heat Stabilized
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide AG4K PA66, 20% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AG4K is a Heat and Hydrolytically Stabilized, 20% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Water Absorption at Saturation 5.5 %

@Temperature 23.0 °C
5.5 %

@Temperature 73.4 °F
ISO 62-1
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Hardness, Rockwell L 112
112
ISO 2039-2
Tensile Strength at Break 130 MPa
18900 psi
5 mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
5 mm/min; ISO 527
Tensile Modulus 7.00 GPa
1020 ksi
1 mm/min; ISO 527
Flexural Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Modulus 6.80 GPa
986 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
80x10x4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1A
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
Edgew 80x10x4; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 31.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
17.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
52.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 255 °C
491 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
Flame Spread 5.00 mm/min

@Thickness 3.00 mm
0.197 in/min

@Thickness 0.118 in
FMVSS Buring Speed
10.0 mm/min

@Thickness 2.00 mm
0.394 in/min

@Thickness 0.0787 in
FMVSS Buring Speed
Oxygen Index 27 %
27 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 50.0 - 60.0 Hz
3.4

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
483 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0068

@Frequency 50.0 - 60.0 Hz
0.0068

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 400 V
400 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Zone 1
Middle Barrel Temperature 270 - 280 °C
518 - 536 °F
Zone 2
Front Barrel Temperature 270 - 290 °C
518 - 554 °F
Zone 3
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %
Descriptive Properties Value Comments
UL f1 f1