Eurostar Staramide AG7K PA66, 35% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, Heat Stabilized
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide AG7K PA66, 35% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AG7 is a Heat and Hydrolytically Stabilized, 35% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Moisture Absorption 1.10 %

@Temperature 23.0 °C
1.10 %

@Temperature 73.4 °F
50% RH; ISO 62
Water Absorption at Saturation 4.5 %

@Temperature 23.0 °C
4.5 %

@Temperature 73.4 °F
ISO 62-1
Linear Mold Shrinkage, Flow 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Hardness, Rockwell L 114
114
ISO 2039-2
Tensile Strength at Break 180 MPa
26100 psi
5 mm/min; ISO 527
Elongation at Break 3.3 %
3.3 %
5 mm/min; ISO 527
Tensile Modulus 10.5 GPa
1520 ksi
1 mm/min; ISO 527
Flexural Strength 280 MPa
40600 psi
2 mm/min; ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -40.0 °C
4.28 ft-lb/in²

@Temperature -40.0 °F
80x10x4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1A
11.0 kJ/m²

@Temperature -20.0 °C
5.23 ft-lb/in²

@Temperature -4.00 °F
80x10x4; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1A
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
12.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
43.3 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 258 °C
496 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 255 °C
491 °F
B/120; ISO 306
256 °C
493 °F
B/50; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
Flame Spread 2.00 mm/min

@Thickness 3.00 mm
0.0787 in/min

@Thickness 0.118 in
FMVSS Buring Speed
6.00 mm/min

@Thickness 2.00 mm
0.236 in/min

@Thickness 0.0787 in
FMVSS Buring Speed
Oxygen Index 27 %
27 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
Glow-Wire Flammability; IEC 60695-2-12
650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
Glow-Wire Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 50.0 - 60.0 Hz
3.4

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
483 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0068

@Frequency 50.0 - 60.0 Hz
0.0068

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 375 V
375 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Zone 1
Middle Barrel Temperature 270 - 280 °C
518 - 536 °F
Zone 2
Front Barrel Temperature 270 - 290 °C
518 - 554 °F
Zone 3
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %
Descriptive Properties Value Comments
Potable Water KTW
UL f1 f1