Eurostar Staramide BG10H PA6, 50% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled , Nylon 6, Heat Stabilized
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BG10H PA6, 50% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BG10 is a Heat Stabilized, 50% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Moisture Absorption 0.600 %

@Temperature 23.0 °C
0.600 %

@Temperature 73.4 °F
50% RH; ISO 62
Water Absorption at Saturation 4.5 %

@Temperature 23.0 °C
4.5 %

@Temperature 73.4 °F
ISO 62-1
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
on Tensile Bar; ISO 294
Linear Mold Shrinkage, Transverse 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Hardness, Rockwell L 122
122
ISO 2039-2
Tensile Strength at Break 224 MPa
32500 psi
5 mm/min; ISO 527
Elongation at Break 3.2 %
3.2 %
5 mm/min; ISO 527
Tensile Modulus 14.0 GPa
2030 ksi
1 mm/min; ISO 527
Flexural Strength 320 MPa
46400 psi
2 mm/min; ISO 178
Flexural Modulus 13.25 GPa
1922 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²

@Temperature -40.0 °C
6.66 ft-lb/in²

@Temperature -40.0 °F
Edgew 80x10x4 sp=62; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 180/1A
16.0 kJ/m²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
Edgew 80x10x4 sp=62; ISO 180/1A
18.0 kJ/m²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 180/1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1U
90.0 kJ/m²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1U
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
10.0 J/cm²

@Temperature -30.0 °C
47.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
6.67 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 83.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
46.1 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 215 °C
419 °F
B/120; ISO 306
218 °C
424 °F
B/50; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
Oxygen Index 25 %
25 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 50.0 - 60.0 Hz
3.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
508 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0061

@Frequency 50.0 - 60.0 Hz
0.0061

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.016

@Frequency 1.00e+6 Hz
0.016

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 350 V
350 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Zone 1
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 2
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Zone 3
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %