Eurostar Staramide BG4ST43 PA6, Glass Fiber Filled, Impact Modified, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BG4ST43 PA6, Glass Fiber Filled, Impact Modified, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide BG4ST43 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 1.40 %

@Temperature 23.0 °C
1.40 %

@Temperature 73.4 °F
50% RH; ISO 62
Water Absorption at Saturation 6.0 %

@Temperature 23.0 °C
6.0 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm
0.0070 - 0.0090 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, H358/30 101 MPa
14600 psi
ISO 2039-1
Tensile Strength at Break 83.0 MPa
12000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 85.0 MPa
12300 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527
Elongation at Yield 3.2 %
3.2 %
5 mm/min; ISO 527
Tensile Modulus 5.00 GPa
725 ksi
1 mm/min; ISO 527
Flexural Strength 115 MPa
16700 psi
2 mm/min; ISO 178
Flexural Modulus 4.00 GPa
580 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1A
12.0 kJ/m²

@Temperature -40.0 °C
5.71 ft-lb/in²

@Temperature -40.0 °F
80x10x4; ISO 180/1A
14.0 kJ/m²

@Temperature -20.0 °C
6.66 ft-lb/in²

@Temperature -4.00 °F
80x10x4; ISO 180/1A
18.0 kJ/m²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1U
55.0 kJ/m²

@Temperature -30.0 °C
26.2 ft-lb/in²

@Temperature -22.0 °F
80x10x4; ISO 180/1U
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
1.70 J/cm²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
Edgew 80x10x4 sp=62; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 31

@Load 1.00 kg
31

@Load 2.20 lb
CS-17; E2P Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 180 µm/m-°C

@Temperature 23.0 - 60.0 °C
100 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 185 °C
365 °F
B/50; ISO 306
186 °C
367 °F
B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 240 - 250 °C
464 - 482 °F
Zone 3 240 - 260 °C
464 - 500 °F
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %