Eurostar Staramide RF006S-GY9A121 PA66, 30% Glass Fiber Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide RF006S-GY9A121 PA66, 30% Glass Fiber Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide RF006S-GY9A121 is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 4.00 mm
 0.0030 - 0.0050 in/in

@Thickness 0.157 in
 E2P method
Mechanical Properties Metric English Comments
Tensile Strength at Break 133 MPa
19300 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ISO 527
Flexural Strength 188 MPa
27300 psi
ISO 178
Flexural Modulus 7.40 GPa
1070 ksi
ISO 178
Izod Impact, Notched (ISO) 4.50 kJ/m²
2.14 ft-lb/in²
80x10x4; ISO 179/1eA
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Processing Properties Metric English Comments
Zone 1 260 - 280 °C
500 - 536 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 290 °C
518 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %