Eurostar Starflam AFR450X2 PA66, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam AFR450X2 PA66, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AFR450X2 is a Red Phosphorous, Flame Retardant, 25% Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption 1.20 %

@Temperature 23.0 °C
 1.20 %

@Temperature 73.4 °F
 50% RH; ISO 62
Water Absorption at Saturation 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Hardness, Rockwell L 108
108
ISO 2039-2
Tensile Strength at Break 160 MPa
23200 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 8.70 GPa
1260 ksi
1 mm/min; ISO 527
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
Flexural Modulus 8.00 GPa
1160 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
9.00 kJ/m²

@Temperature -20.0 °C
 4.28 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 15.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 248 °C
478 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 245 °C
473 °F
B/120; ISO 306
245 °C
473 °F
B/50; ISO 306
UL RTI, Electrical 110 °C

@Thickness 0.750 mm
 230 °F

@Thickness 0.0295 in
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness 0.750 mm
 230 °F

@Thickness 0.0295 in
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
 IEC 60695-11-10
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0054

@Frequency 50.0 - 60.0 Hz
 0.0054

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0119

@Frequency 1.00e+6 Hz
 0.0119

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.750 mm
 >= 120 sec

@Thickness 0.0295 in
 PLC 0
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 PLC 0
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 275 - 285 °C
527 - 545 °F
Zone 1
Middle Barrel Temperature 275 - 285 °C
527 - 545 °F
Zone 2
Front Barrel Temperature 275 - 285 °C
527 - 545 °F
Zone 3
Melt Temperature 275 - 285 °C
527 - 545 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.10 %
0.10 %