Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Eurostar Starflam PW0042E PA6, 20% Mineral Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam PW0042E PA6, 20% Mineral Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PW0042E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Mineral Reinforced, Polyamide 6 Injection MoldingInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Time 86400 sec
0.0050 - 0.0080 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
Tensile Modulus 6.40 GPa
928 ksi
1 mm/min; ISO 527
Flexural Strength 130 MPa
18900 psi
ISO 178
Flexural Modulus 6.00 GPa
870 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
IEC 60695-11-10
Glow Wire Test 960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
IEC 60695-2-12
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 1
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 2
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Zone 3
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %