Eurostar Starflam RF0055E PA66/6, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam RF0055E PA66/6, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam RF0055E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z250EM)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.80 GPa
1420 ksi
1 mm/min; ISO 527
Flexural Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Modulus 8.40 GPa
1220 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Hot Ball Pressure Test 210 °C

@Thickness 3.00 mm
 410 °F

@Thickness 0.118 in
 IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 65.0 °C

@Thickness 1.00 mm
 149 °F

@Thickness 0.0394 in
 ALL
65.0 °C

@Thickness 1.20 mm
 149 °F

@Thickness 0.0472 in
 ALL
65.0 °C

@Thickness 1.50 - 1.65 mm
 149 °F

@Thickness 0.0591 - 0.0650 in
 ALL
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 NC
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.00 mm
 149 °F

@Thickness 0.0394 in
 ALL
65.0 °C

@Thickness 1.20 mm
 149 °F

@Thickness 0.0472 in
 ALL
65.0 °C

@Thickness 1.50 - 1.65 mm
 149 °F

@Thickness 0.0591 - 0.0650 in
 ALL
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 NC
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.00 mm
 149 °F

@Thickness 0.0394 in
 ALL
65.0 °C

@Thickness 1.20 mm
 149 °F

@Thickness 0.0472 in
 ALL
65.0 °C

@Thickness 1.50 - 1.65 mm
 149 °F

@Thickness 0.0591 - 0.0650 in
 ALL
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 NC
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 ALL; IEC 60695-11-10
V-0

@Thickness 1.20 mm
 V-0

@Thickness 0.0472 in
 ALL; IEC 60695-11-10
V-0

@Thickness 1.50 - 1.65 mm
 V-0

@Thickness 0.0591 - 0.0650 in
 ALL; IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 NC; IEC 60695-11-10
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 Glow-Wire Ignition; IEC 60695-2-13
850 °C

@Thickness 1.50 - 1.65 mm
 1560 °F

@Thickness 0.0591 - 0.0650 in
 Glow-Wire Ignition; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
 1560 °F

@Thickness 0.118 in
 Glow-Wire Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC 2
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 1
Middle Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 2
Front Barrel Temperature 270 - 280 °C
518 - 536 °F
Zone 3
Melt Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %