ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications

Category Polymer , Film , Thermoplastic , Elastomer, TPE
Manufacturer Exxon Chemical
Trade Name EXACT™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Exact 3128 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. It is designed fro both monolayer and multilayer coextruded blown film applications requiring excellent toughness and good heat sealing performance.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications:Blown FilmCheese PackagingLamination FilmMeat PackagingPoultry Bag Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ExxonMobil Method
Thickness 31.8 microns
1.25 mil
Melt Flow 1.3 g/10 min
1.3 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 4.83 MPa
700 psi
ASTM D882
Film Tensile Strength at Yield, TD 4.41 MPa
640 psi
ASTM D882
Film Elongation at Break, MD 560 %
560 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Film Elongation at Yield, MD 9.2 %
9.2 %
ASTM D882
Film Elongation at Yield, TD 7.9 %
7.9 %
ASTM D882
Puncture Energy 8.08 J
5.96 ft-lb
ExxonMobil Method
Elmendorf Tear Strength, MD 3.78 g/micron
96.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 6.93 g/micron
176 g/mil
ASTM D1922
Dart Drop 21.1 g/micron
536 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 60.4 MPa
8760 psi
ASTM D882
Film Tensile Strength at Break, TD 52.3 MPa
7580 psi
ASTM D882
1% Secant Modulus, MD 73.1 MPa
10600 psi
ASTM D882
1% Secant Modulus, TD 77.2 MPa
11200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 92.2 °C
198 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 73.0 °C
163 °F
ExxonMobil Method
Vicat Softening Point 83.9 °C
183 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.5 %
3.5 %
ASTM D1003
Gloss 77 %
77 %
ASTM D2457
Descriptive Properties Value Comments
Puncture Force 16 lbf
ExxonMobil Method