ExxonMobil Escorene™ FL 00206 Ethylene Vinyl Acetate Copolymer (European Grade)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ FL 00206 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FL 00206 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 280°C (536°F) may cause resin degradation. Machines should always be purged with LDPE or suitable cleaning compound before shutdown.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: No Applications: Co-Extrusion FilmsInjection Molding Form Fill and Seal PackagingSkin PackagingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ExxonMobil method
Vinyl Acetate Content 6.5 %
6.5 %
ExxonMobil method
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 94
94
Molded Properties; ISO 868
Tensile Strength at Break >= 0.689 MPa
>= 100 psi
Molded Properties; ISO 527-2/1A
Film Elongation at Break, MD 400 %
400 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Tensile Modulus 0.103 GPa
15.0 ksi
Molded Properties; ISO 527-2/1A/1
Elmendorf Tear Strength MD 130 g
130 g
ASTM D1922
Elmendorf Tear Strength TD 130 g
130 g
ASTM D1922
Dart Drop Test 280 g
0.617 lb
ASTM D1709A
Film Tensile Strength at Break, MD 24.1 MPa
3500 psi
ASTM D882
Film Tensile Strength at Break, TD 22.1 MPa
3200 psi
ASTM D882
1% Secant Modulus, MD 117 MPa
17000 psi
ASTM D882
1% Secant Modulus, TD 138 MPa
20000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 212 °C
<= 414 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 81.1 °C
178 °F
ASTM D1525