ExxonMobil Escorene™ FL 00218 Ethylene Vinyl Acetate Copolymer (European Grade)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ FL 00218 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FL 00218 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 240°C (464°F) may cause resin degradation. Machines should always be purged with LDPE or suitable cleaning compound before shutdown.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Free Flowing Agent: No Applications:Agricultural FilmBlown FilmCast FilmCo-Extrusion FilmsExtrusion CoatingLamination FilmTube ExtrusionInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.941 g/cc
0.0340 lb/in³
ExxonMobil method
Vinyl Acetate Content 18 %
18 %
ExxonMobil method
Melt Flow 1.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Elmendorf Tear Strength MD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength TD 180 g
180 g
ASTM D1922
Dart Drop Test 690 g
1.52 lb
ASTM D1709A
Film Tensile Strength at Break, MD 39.3 MPa
5700 psi
ASTM D882
Film Tensile Strength at Break, TD 33.8 MPa
4900 psi
ASTM D882
1% Secant Modulus, MD 50.3 MPa
7300 psi
ASTM D882
1% Secant Modulus, TD 50.3 MPa
7300 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 187 °C
<= 369 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 62.2 °C
144 °F
ASTM D1525
Descriptive Properties Value Comments
Blending Temperature 240