ExxonMobil Escorene™ FL 01418 Ethylene Vinyl Acetate Copolymer (European Grade)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ FL 01418 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FL 01418 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 01418 is an excellent sealing material with a very low seal initiation temperature and high clarity.Processing Conditions: Excellent results are obtained in extrusion coating at 225°C (437°F) temperature range. Processing temperatures above 240°C (464°F) may cause resin degradation. FL 01418 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications:Adhesive LaminationBarrier Food Packaging Coextrusion Coating CompoundingDocument PlastificationExtrusion CoatingExtrusion LaminationFlexible PackagingHigh Frequency SealingIndustrial PackagingInjection MoldingMasterbatch Base ResinNon-Woven CoatingPVC ReplacementThermal LaminationWire and Cable Compounds Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.938 g/cc
0.0339 lb/in³
ExxonMobil method
Vinyl Acetate Content 18 %
18 %
ExxonMobil method
Melt Flow 14 g/10 min
14 g/10 min
ASTM D1238
Neck In 8.64 cm

@Temperature 230 °C
3.40 in

@Temperature 446 °F
656 ft/min, constant output at 35 rpm; ExxonMobil Method
9.40 cm

@Temperature 230 °C
3.70 in

@Temperature 446 °F
328 ft/min, constant output at 35 rpm; ExxonMobil Method
Drawdown 8.17 m/s

@Temperature 230 °C
1610 ft/min

@Temperature 446 °F
Constant output at 35 rpm; ExxonMobil Method
Mechanical Properties Metric English Comments
Hardness, Shore A 87

@Time 15.0 sec
87

@Time 0.00417 hour
Molded Properties; ISO 868
Tensile Strength at Break >= 0.689 MPa
>= 100 psi
Molded Properties; ISO 527-2/1A
Tensile Modulus 0.0331 GPa
4.80 ksi
Molded Properties; ISO 527-2
Thermal Properties Metric English Comments
Melting Point <= 180 °C
<= 356 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 52.2 °C
126 °F
ASTM D1525
Descriptive Properties Value Comments
Blending Temperature 240