ExxonMobil Escorene® LD-307 EVA Film Resin, Clarity, High Impact  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-307 EVA Film Resin, Clarity, High Impact  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 5.0% vinyl acetate copolymer, clarity film resin. Film made from this resin has superior impact strength and heat sealability.Applications: Frozen food packaging; Other food packaging such as heavy duty produce bags, rice bags, poultry bags, etc.; High strength bags; Applications requiring excellent toughness and good heat sealability. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.60 MPa
1100 psi
ASTM D882
Film Tensile Strength at Yield, TD 6.90 MPa
1000 psi
ASTM D882
Film Elongation at Break, MD 150 %
150 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Secant Modulus, MD 0.120 GPa
17.4 ksi
ASTM D882
Secant Modulus, TD 0.140 GPa
20.3 ksi
ASTM D882
Elmendorf Tear Strength MD 275 g
275 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Elmendorf Tear Strength, MD 8.66 g/micron
220 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.15 g/micron
80.0 g/mil
ASTM D1922
Dart Drop 3.46 g/micron
88.0 g/mil
F50; ASTM D1709
Dart Drop Test 110 g
0.243 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 24.0 MPa
3480 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 103 °C
217 °F
Exxon Method
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 60 %
60 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified