ExxonMobil Escorene® LD-708 EVA Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-708 EVA Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 15.5% vinyl acetate copolymer film resin. Film made from LD-708 exhibits good impact strength and superior heat sealability.Applications: Primal meat bags; Processed meat and cheese packaging. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 5.2 g/10 min
5.2 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 15.0 MPa
2180 psi
ASTM D882
Film Tensile Strength at Yield, TD 4.50 MPa
653 psi
ASTM D882
Film Elongation at Break, MD 190 %
190 %
ASTM D882
Film Elongation at Break, TD 760 %
760 %
ASTM D882
Secant Modulus, MD 0.136 GPa
19.7 ksi
ASTM D882
Secant Modulus, TD 0.100 GPa
14.5 ksi
ASTM D882
Elmendorf Tear Strength MD 320 g
320 g
ASTM D1922
Elmendorf Tear Strength TD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength, MD 10.1 g/micron
256 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.52 g/micron
64.0 g/mil
ASTM D1922
Dart Drop 2.20 g/micron
56.0 g/mil
F50; ASTM D1709
Dart Drop Test 70.0 g
0.154 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 34.0 MPa
4930 psi
ASTM D882
Film Tensile Strength at Break, TD 18.0 MPa
2610 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 88.0 °C
190 °F
Exxon Method
Optical Properties Metric English Comments
Haze 1.3 %
1.3 %
ASTM D1003
Gloss 87 %
87 %
45°, ASTM D-2457