ExxonMobil Escorene® LD 713.93 Cast Film Resin

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Exxon Chemical
Trade Name	Escorene®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 713.93 Cast Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer film resin. Film made from LD 713.93 exhbits very high impact strength, hihg clarity, and excellent heat sealabilityAvailability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications:Heat Seal LayerMeat PackagingInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.933 g/cc	0.0337 lb/in³	ExxonMobil Method
Vinyl Acetate Content	14.4 %	14.4 %	ExxonMobil Method
Melt Flow	3.50 g/10 min @Load 2.16 kg, Temperature 190 °C	3.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	870 %	870 %	ASTM D882
Elmendorf Tear Strength, MD	7.68 g/micron	195 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	2.76 g/micron	70.0 g/mil	ASTM D1922
Dart Drop	1.97 g/micron	50.0 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	33.6 MPa	4880 psi	ASTM D882
Film Tensile Strength at Break, TD	19.0 MPa	2750 psi	ASTM D882
1% Secant Modulus, MD	110 MPa	15900 psi	ASTM D882
1% Secant Modulus, TD	101 MPa	14600 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	87.8 °C	190 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	63.9 °C	147 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	2.0 %	2.0 %	ASTM D1003
Gloss	81 %	81 %	45°; ASTM D2457