ExxonMobil Escorene® LD 767.MJ Molding, extrusion and compounding resin (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 767.MJ Molding, extrusion and compounding resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 767.MJ is a high viscosity, 29.5% vinyl acetate copolymer suitable for making very soft, blow molded or extruded articles with very good low temperature toughness. It can also be used as a polymer modifier to make specialty compounds.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.954 g/cc	0.0345 lb/in³	ExxonMobil Method
Vinyl Acetate Content	29.5 %	29.5 %	ExxonMobil Method
Melt Flow	3.1 g/10 min	3.1 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	74	74	15s; ASTM D2240
Hardness, Shore D	26	26	15s; ASTM D2240
Tensile Strength at Break	9.58 MPa	1390 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0241 GPa	3.49 ksi	1% secant; ASTM D790
Impact Test	16.3 J @Temperature 23.0 °C	12.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	38.0 J @Temperature -40.0 °C	28.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	69.4 °C	157 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	43.9 °C	111 °F	ASTM D1525

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer