ExxonMobil Escorene® LD-768 High EVA Film and Compounding Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-768 High EVA Film and Compounding Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A low gel 27.5% vinyl acetate copolymer designed for film and compounding applications. The resin provides very low modulus films with high tensile strength and impact strength.Applications: Low modulus films; Elastic films; Compounding; Batch inclusion bags; Radio frequency weldable films. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.951 g/cc
0.0344 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.3 g/10 min
2.3 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 3.00 MPa
435 psi
ASTM D882
Film Tensile Strength at Yield, TD 2.00 MPa
290 psi
ASTM D882
Film Elongation at Break, MD 330 %
330 %
ASTM D882
Film Elongation at Break, TD 640 %
640 %
ASTM D882
Secant Modulus, MD 0.0300 GPa
4.35 ksi
ASTM D882
Secant Modulus, TD 0.0400 GPa
5.80 ksi
ASTM D882
Elmendorf Tear Strength MD 160 g
160 g
ASTM D1922
Elmendorf Tear Strength TD 30 g
30 g
ASTM D1922
Elmendorf Tear Strength, MD 5.04 g/micron
128 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 0.945 g/micron
24.0 g/mil
ASTM D1922
Dart Drop 12.9 g/micron
328 g/mil
F50; ASTM D1709
Dart Drop Test 410 g
0.904 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 75.0 °C
167 °F
Exxon Method
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
ASTM D1003
Gloss 80 %
80 %
45°, ASTM D-2457