ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.An LLDPE blown film resin. Films made from LL-1117 have very good tensile properties and toughness. This resin's good strength and drawability allow downgauging in many film applications. This resin is formulated with several stabilization packages.Applications: Soft goods overwrap; Liners; Bakery products overwrap; Laminating film; Packaging film; Sandwich bags. Data for film properties below based on 1.2 mil film.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
Exxon Method
Thickness 30.5 microns
1.20 mil
Melt Flow 1.5 g/10 min
1.5 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.0 MPa
1740 psi
ASTM D882
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
Film Elongation at Break, MD 670 %
670 %
ASTM D882
Film Elongation at Break, TD 790 %
790 %
ASTM D882
Secant Modulus, MD 0.296 GPa
42.9 ksi
ASTM D882
Secant Modulus, TD 0.324 GPa
47.0 ksi
ASTM D882
Elmendorf Tear Strength MD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength TD 300 g
300 g
ASTM D1922
Elmendorf Tear Strength, MD 2.64 g/micron
67.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 9.84 g/micron
250 g/mil
ASTM D1922
Dart Drop 2.28 g/micron
58.0 g/mil
F50; ASTM D1709
Dart Drop Test 70.0 g
0.154 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 46.0 MPa
6670 psi
ASTM D882
Film Tensile Strength at Break, TD 37.0 MPa
5370 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Exxon Method
Optical Properties Metric English Comments
Haze 16 %
16 %
ASTM D1003
Gloss 46 %
46 %
45°, ASTM D-2457