ExxonMobil Exceed™ 3518 GA Premium Cast Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 3518 GA Premium Cast Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceed 3518 resins are hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 3518 resins have outstanding tensile properties and impact and puncture toughness. These superior properties, along with excellent drawability, make these resins versatile for both monolayer and multilayer cast packaging film.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 20.3 microns
0.800 mil
Melt Flow 3.5 g/10 min
3.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.27 MPa
1200 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 7.58 MPa
1100 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 510 %
510 %
ASTM D882
Film Elongation at Break, TD 680 %
680 %
ASTM D882
Puncture Energy 4.30 J
3.17 ft-lb
Exxon Mobil Method
Elmendorf Tear Strength MD 190 g
190 g
ASTM D1922
Elmendorf Tear Strength TD 500 g
500 g
ASTM D1922
Elmendorf Tear Strength, MD 9.350 g/micron
237.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 24.6 g/micron
625 g/mil
ASTM D1922
Dart Drop 6.89 g/micron
175 g/mil
ASTM D1709
Dart Drop Test 140 g
0.309 lb
ASTM D1709
Film Tensile Strength at Break, MD 73.8 MPa
10700 psi
ASTM D882
Film Tensile Strength at Break, TD 46.7 MPa
6770 psi
ASTM D882
1% Secant Modulus, MD 110 MPa
16000 psi
ASTM D882
1% Secant Modulus, TD 124 MPa
18000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 114 °C
237 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 2.4 %
2.4 %
ASTM D1003
Gloss 86 %
86 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer