ExxonMobil Exceed™ 399L60 LDPE/Hexene Premium Blown Film Resin, 3 mil Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 399L60 LDPE/Hexene Premium Blown Film Resin, 3 mil Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 399L60 resin have balanced tensile, impact strength, tear and puncture.Applications: Trash bags; Liners; Heavy duty bags. Data for film properties below based on 3 mil film.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
Exxon Method
Thickness 76.2 microns
3.00 mil
Melt Flow 0.75 g/10 min
0.75 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.3 MPa
1780 psi
ASTM D882
Film Tensile Strength at Yield, TD 12.7 MPa
1840 psi
ASTM D882
Film Elongation at Break, MD 640 %
640 %
ASTM D882
Film Elongation at Break, TD 660 %
660 %
ASTM D882
Secant Modulus, MD 0.326 GPa
47.3 ksi
ASTM D882
Secant Modulus, TD 0.356 GPa
51.6 ksi
ASTM D882
Coefficient of Friction 0.60
0.60
ASTM D1894
Elmendorf Tear Strength MD 820 g
820 g
ASTM D1922
Elmendorf Tear Strength TD 1370 g
1370 g
ASTM D1922
Elmendorf Tear Strength, MD 10.7 g/micron
273 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 18.0 g/micron
457 g/mil
ASTM D1922
Dart Drop 10.6 g/micron
270 g/mil
F50; ASTM D1709
Dart Drop Test 810 g
1.79 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 54.0 MPa
7830 psi
ASTM D882
Film Tensile Strength at Break, TD 53.0 MPa
7690 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 121 °C
250 °F
Exxon Method
Optical Properties Metric English Comments
Haze 27.5 %
27.5 %
ASTM D1003
Gloss 35 %
35 %
45°, ASTM D-2457