ExxonMobil Exxtral™ LNU 011 Performance Polyolefin

Category	Polymer , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer	Exxon Chemical
Trade Name	Exxtral™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exxtral™ LNU 011 Performance Polyolefin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A specialty thermoplastic polyolefin resin with high stiffness, high gloss, low discoloration and good detergent resistance for large electrical appliances such as washing machines.Availability: Africa & Middle East, Asia Pacific, Europe, North America and South America Features:Good Mold ReleaseGood Surface Finish Uses: Appliance ComponentsAppliances Consumer ApplicationsProcessing Method: Injection MoldingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.930 g/cc	0.0336 lb/in³	ISO 1183
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 °C	10 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	38.0 MPa	5510 psi	ISO 527-2/50
Elongation at Yield	>= 6.0 %	>= 6.0 %	ISO 527-2/50
Tensile Modulus	2.00 GPa	290 ksi	Secant; ISO 527-2
Flexural Modulus	1.90 GPa	276 ksi	Secant; ISO 178
Charpy Impact Unnotched	1.60 J/cm² @Temperature -30.0 °C	7.60 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	2.10 J/cm² @Temperature 0.000 °C	10.0 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eU
	10.1 J/cm² @Temperature 22.8 °C	48.0 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.149 J/cm² @Temperature -30.0 °C	0.710 ft-lb/in² @Temperature -22.0 °F	ISO 179
	0.181 J/cm² @Temperature 0.000 °C	0.860 ft-lb/in² @Temperature 32.0 °F	ISO 179
	0.357 J/cm² @Temperature 22.8 °C	1.70 ft-lb/in² @Temperature 73.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	120 °C	248 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-2/A