ExxonMobil HD 7960.13 HMW Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil HD 7960.13 HMW Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HD 7960.13 is a high molecular weight HDPE blown film resin. Films made from HD 7960.13 exhibit excellent impact and toughness properties, as well as high stiffness. HD 7960.13 is particularly recommended for films less than 0.5 mil in thickness.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: Blown FilmGrocery SacksInstitutional Can LinersMerchandise BagsProduce Bags on a RollTrash BagsInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ExxonMobil Method
Melt Flow 0.60 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
High Load Melt Index 10 g/10 min

@Load 21.6 kg,
Temperature 190 °C
10 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 37.9 MPa
5500 psi
ASTM D882
Film Tensile Strength at Yield, TD 33.1 MPa
4800 psi
ASTM D882
Film Elongation at Break, MD 270 %
270 %
ASTM D882
Film Elongation at Break, TD 380 %
380 %
ASTM D882
Elmendorf Tear Strength MD 7.0 g
7.0 g
ASTM D1922
Elmendorf Tear Strength TD 30 g
30 g
ASTM D1922
Dart Drop 23.6 g/micron
600 g/mil
ASTM D1709
Dart Drop Test 300 g
0.662 lb
ASTM D1709A
Film Tensile Strength at Break, MD 82.7 MPa
12000 psi
ASTM D882
Film Tensile Strength at Break, TD 68.9 MPa
10000 psi
ASTM D882
1% Secant Modulus, MD 1030 MPa
150000 psi
ASTM D882
1% Secant Modulus, TD 1100 MPa
160000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 131 °C
267 °F
Peak Melting Temperature; ExxonMobil Method
Descriptive Properties Value Comments
Features Thermal Stabilizer