ExxonMobil LD 071.MU Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 071.MU Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 071 series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, toughness, burn-through resistance and clarity.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.70 g/10 min
0.70 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.4 MPa
1650 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 11.8 MPa
1710 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 230 %
230 %
ASTM D882
Film Elongation at Break, TD 630 %
630 %
ASTM D882
Film Elongation at Yield, MD 6.0 %
6.0 %
ASTM D882
Film Elongation at Yield, TD 5.1 %
5.1 %
ASTM D882
Elmendorf Tear Strength MD 430 g
430 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength, MD 8.46 g/micron
215 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.95 g/micron
75.0 g/mil
ASTM D1922
Dart Drop 3.35 g/micron
85.0 g/mil
ASTM D1709
Dart Drop Test 170 g
0.375 lb
ASTM D1709
Film Tensile Strength at Break, MD 27.9 MPa
4040 psi
ASTM D882
Film Tensile Strength at Break, TD 27.1 MPa
3930 psi
ASTM D882
1% Secant Modulus, MD 232 MPa
33700 psi
ASTM D882
1% Secant Modulus, TD 197 MPa
28600 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 112 °C
234 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 99.0 °C
210 °F
ExxonMobil Method
Vicat Softening Point 97.2 °C
207 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 65 %
65 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer