ExxonMobil LD 136.MV Packaging Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 136.MV Packaging Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 136 series resins are homopolymer film resins with good clarity. They are suitable for processing in cast film equipment. Applications include food packaging, textile packaging, and other packaging applications requiring good clarity.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.7 MPa
1550 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 10.7 MPa
1550 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 130 %
130 %
ASTM D882
Film Elongation at Break, TD 540 %
540 %
ASTM D882
Film Elongation at Yield, MD 8.5 %
8.5 %
ASTM D882
Film Elongation at Yield, TD 5.8 %
5.8 %
ASTM D882
Elmendorf Tear Strength, MD 12.2 g/micron
310 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.60 g/micron
66.0 g/mil
ASTM D1922
Dart Drop 2.83 g/micron
72.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 25.4 MPa
3680 psi
ASTM D882
Film Tensile Strength at Break, TD 19.1 MPa
2770 psi
ASTM D882
1% Secant Modulus, MD 200 MPa
29000 psi
ASTM D882
1% Secant Modulus, TD 248 MPa
36000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 111 °C
232 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 92.2 °C
198 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 66 %
66 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer