ExxonMobil LD 312.23 High Impact Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 312.23 High Impact Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 312 Series films have superior impact strength, good heat sealability, and good low temperature properties. Applications include frozen and other food packaging.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ExxonMobil Method
Vinyl Acetate Content 4.6 %
4.6 %
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ExxonMobil Method
Antiblock Level 5000 ppm
5000 ppm
Slip Level 1100 ppm
1100 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.27 MPa
1200 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 7.93 MPa
1150 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 180 %
180 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Film Elongation at Yield, MD 6.9 %
6.9 %
ASTM D882
Film Elongation at Yield, TD 5.6 %
5.6 %
ASTM D882
Elmendorf Tear Strength MD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength TD 90 g
90 g
ASTM D1922
Elmendorf Tear Strength, MD 5.248 g/micron
133.3 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.36 g/micron
60.0 g/mil
ASTM D1922
Dart Drop 4.984 g/micron
126.6 g/mil
ASTM D1709
Dart Drop Test 190 g
0.419 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.9 MPa
3760 psi
ASTM D882
Film Tensile Strength at Break, TD 24.7 MPa
3580 psi
ASTM D882
1% Secant Modulus, MD 146 MPa
21200 psi
ASTM D882
1% Secant Modulus, TD 168 MPa
24400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 104 °C
220 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 91.0 °C
196 °F
ExxonMobil Method
Vicat Softening Point 88.9 °C
192 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.4 %
6.4 %
ASTM D1003
Gloss 71 %
71 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer