ExxonMobil LD 419.MV Wire & Cable Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 419.MV Wire & Cable Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.921 g/cc	0.0333 lb/in³	ExxonMobil Method
Melt Flow	2.25 g/10 min	2.25 g/10 min	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	90	90	15s; ASTM D2240
Hardness, Shore D	44	44	15s; ASTM D2240
Tensile Strength at Break	10.3 MPa	1500 psi	ASTM D638
Tensile Strength, Yield	11.6 MPa	1680 psi	ASTM D638
Elongation at Break	625 %	625 %	ASTM D638
Elongation at Yield	14 %	14 %	ASTM D638
1% Secant Modulus	243 MPa	35200 psi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	109 °C	228 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	93.9 °C	201 °F	ASTM D1525

Electrical Properties	Metric	English	Comments
Volume Resistivity	7.61e+15 ohm-cm	7.61e+15 ohm-cm	ASTM D257
Dielectric Constant	2.17 @Frequency 60 Hz	2.17 @Frequency 60 Hz	ASTM D150
Dielectric Strength	49.6 kV/mm	1260 kV/in	ASTM D149
Dissipation Factor	0.000010 @Frequency 60 Hz	0.000010 @Frequency 60 Hz	ASTM D150

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer