ExxonMobil LDPE LD 312.82 Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 312.82 Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 312 resins are 4.6% vinyl acetate copolymers for films with good toughness. The comonomer content and low melt index of those resins help produce films which exhibit superior impact strength, good heat sealability and good low temperature properties.Availability: Latin America, North America and South America Additive: Antiblock: 4000 ppmSlip: 800 ppm Thermal Stabilizer: YesApplications: Coextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmLamination FilmPoultry BagProduce BagsRice BagsInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil method
Vinyl Acetate Content	4.6 %	4.6 %	ExxonMobil Method
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	4000 ppm	4000 ppm
Slip Level	800 ppm	800 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	170 %	170 %	ASTM D882
Film Elongation at Break, TD	560 %	560 %	ASTM D882
Puncture Energy	0.463 J	0.342 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	190 g	190 g	ASTM D1922
Elmendorf Tear Strength TD	90 g	90 g	ASTM D1922
Dart Drop Test	200 g	0.441 lb	ASTM D1709A
Film Tensile Strength at Break, MD	248 MPa	36000 psi	ASTM D882
Film Tensile Strength at Break, TD	23.4 MPa	3400 psi	ASTM D882
1% Secant Modulus, MD	138 MPa	20000 psi	ASTM D882
1% Secant Modulus, TD	165 MPa	24000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 221 °C	<= 430 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	8.5 %	8.5 %	ASTM D1003
Gloss	66 %	66 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	7 lbf	ExxonMobil Method