ExxonMobil LDPE LGA 105 Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LGA 105 Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LGA 105 is a homopolymer, garment film resin with good toughness. It is capable of being draw-down to thin gauges.Availability: North America Additive: Antiblock: NoSlip: NoProcessing Aid: NoThermal Stabilizer: NoApplications: Blown FilmCast FilmCompoundingGarment FilmHygiene FilmLaundry FilmInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 6.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.96 MPa
1300 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.96 MPa
1300 psi
ASTM D882
Film Elongation at Break, MD 390 %
390 %
ASTM D882
Film Elongation at Break, TD 680 %
680 %
ASTM D882
Puncture Energy 1.24 J
0.917 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 440 g
440 g
ASTM D1922
Elmendorf Tear Strength TD 200 g
200 g
ASTM D1922
Dart Drop Test 80.0 g
0.176 lb
ASTM D1709A
Film Tensile Strength at Break, MD 20.7 MPa
3000 psi
ASTM D882
Film Tensile Strength at Break, TD 17.9 MPa
2600 psi
ASTM D882
1% Secant Modulus, MD 165 MPa
24000 psi
ASTM D882
1% Secant Modulus, TD 200 MPa
29000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 231 °C
<= 448 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 4.3 %
4.3 %
ASTM D1003
Gloss 82 %
82 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 8 lbf
ExxonMobil Method