ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Exxon Chemical
Trade Name LLDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 4004EL is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. Sufficient Cu-inhibitor should be added to meet specific ageing requirements for insulation. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: Halogen-free flame retardant (HFFR) compoundsLV silane cross-linkable insulation – 1 step processLV silane cross-linkable insulation – 2-step processTelecom thermoplastic jacketingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ExxonMobil method
Melt Flow 3.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 51

@Time 15.0 sec
51

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 10.3 MPa
1500 psi
ASTM D638
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
Elongation at Break 540 %
540 %
ASTM D638
Elongation at Yield 10 %
10 %
ASTM D638
Flexural Modulus, 1% Secant 338 MPa
49000 psi
ASTM D790
Thermal Properties Metric English Comments
Melting Point <= 252 °C
<= 486 °F
Peak Melting Point; ExxonMobil method
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+15 ohm-cm
6.00e+15 ohm-cm
ASTM D257
Dielectric Constant 2.2

@Frequency 60.0 Hz
2.2

@Frequency 60.0 Hz
ASMT D150
Dielectric Strength 55.1 kV/mm
1400 kV/in
ASTM D149
Dissipation Factor 0.00050

@Frequency 60.0 Hz
0.00050

@Frequency 60.0 Hz
ASMT D150