ExxonMobil Label-Lyte™ 40LH247 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte™ 40LH247 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque, caviated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. LH247 also shows good performances on reel-fed wrap-around labeling machines, where its high stiffness is particularly appreciated.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding white opaque background and superb white gloss finishGood printability on outside treated sideCompatibility with most adhesive formulationsExcellent stiffness and flex resistanceVery good moisture resistanceGood overall converting, diecutting, and dispensing propertiesApplications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsHealth and Beauty Care Industrial Uses: Pressure Sensitive LabelsReel-Fed LabelsProcessing Method: Inner Web Adhesion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing, UV Letterpress Printing, UV Offset Lithography Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Thickness 40.6 microns
1.60 mil
ExxonMobil Method
Coating Weight 28.5 g/m²
17.8 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 170 %
170 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.70 GPa
247 ksi
MD; ExxonMobil Method
2.80 GPa
406 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.60
0.60
Untreated Surface; ExxonMobil Method
Film Tensile Strength at Break, MD 105 MPa
15200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 185 MPa
26800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 3.0 %

@Temperature 135 °C,
Time 432 sec
3.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 3.0 %

@Temperature 135 °C,
Time 432 sec
3.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 70 %
70 %
45°; ExxonMobil Method
Transmission, Visible 25 %
25 %
ExxonMobil Method
Descriptive Properties Value Comments
Yield 24200 in2/lb