ExxonMobil Pax-Plus™ 3204 Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name Pax-Plus™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Pax-Plus™ 3204 Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Pax-Plus 3204 is a rubber modified high density polyethylene film resin which is used primarily in film requiring good impact strength. It is specially formulated to provide easy tear in the machine direction. Its high Vicat softening point permits it to be used for short times at moderately high temperature.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.941 g/cc
0.0340 lb/in³
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
5.8 g/10 min

@Load 10.0 kg,
Temperature 190 °C
5.8 g/10 min

@Load 22.0 lb,
Temperature 374 °F
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 15.2 MPa
2200 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 700 %
700 %
ASTM D882
Film Elongation at Break, TD 900 %
900 %
ASTM D882
Elmendorf Tear Strength MD 50 g
50 g
ASTM D1922
Elmendorf Tear Strength TD 650 g
650 g
ASTM D1922
Elmendorf Tear Strength, MD 0.984 g/micron
25.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 12.8 g/micron
325 g/mil
ASTM D1922
Dart Drop 4.72 g/micron
120 g/mil
ASTM D1709
Dart Drop Test 240 g
0.529 lb
ASTM D1709
Film Tensile Strength at Break, MD 29.8 MPa
4320 psi
ASTM D882
Film Tensile Strength at Break, TD 26.6 MPa
3860 psi
ASTM D882
1% Secant Modulus, MD 399 MPa
57900 psi
ASTM D882
1% Secant Modulus, TD 484 MPa
70200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 131 °C
267 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 114 °C
237 °F
ExxonMobil Method
Descriptive Properties Value Comments
Features Thermal Stabilizer