ExxonMobil Santoprene® 8211-55M300 Thermoplastic Elastomer (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Santoprene® 8211-55M300 Thermoplastic Elastomer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A soft, colorable, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and good appearance. This grade of Santoprene 8000 TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and completely recyclable.Non-hygroscopic product, requires little to no drying before processing.Neutral, easy coloring formulation.Recommended for applications requiring excellent ozone resistance.Used in sealing applications.Recommended for applications requiring excellent flex fatigue resistance.Compliant to EU Directive 2003/11/EC regarding marketing and use of certain dangerous substances and preparations, specifically pentabromodiphenyl ether or octabromodiphenyl ether.EU Directive 2002/95/EC (RoHS) compliant.Information provided by Advanced Elastomer Systems

Physical Properties	Metric	English	Comments
Specific Gravity	0.930 g/cc	0.930 g/cc	23°C; ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55 @Thickness 2.00 mm	55 @Thickness 0.0787 in	ISO 868
Tensile Strength at Break	4.00 MPa	580 psi	Across Flow; ASTM D412
Tensile Strength, Ultimate	1.79 MPa	260 psi	Across Flow; ASTM D412
Elongation at Break	350 %	350 %	Across Flow; ASTM D412

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 230 °C	347 - 446 °F

Descriptive Properties	Value	Comments
Color	Natural Color
Form	Pellets