Fibre Glast 1100 Light-Weight High-Strength Patching/Filler Compound

Category Polymer , Thermoset , Epoxy , Epoxy, Cast, Unreinforced
Manufacturer Fibre Glast Developments Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fibre Glast 1100 Light-Weight High-Strength Patching/Filler Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Features:Very Light Weight MaterialNon-Hazardous Product - Safe to UseEasily Sanded and Carved with Shop ToolsNegligible ShrinkageNon-Critical, 2 to 1 Ratio by Weight or by VolumeExcellent Non-Sag Properties - Even Upside DownSlightly Flexible Cure - Not Brittle in Thin SectionsExcellent Adhesion to a Variety of SurfacesStable Formula - No Separation of Components in StorageDescription:#1100 is a two-component paste epoxy patching and filler compound for foam, wood, fiberglass, and other surfaces. The mixed consistency of this system is very smooth and creamy, so it spreads easily, and can be splined to a feather edge without separation. It is a thixotropic, non-sag material that will remain in place in thick sections, even when applied upside down. The resin and hardener of this system are color coded for easy mixing. The resin is white and the hardener is brown, giving a good visual indication of complete mixing with a uniform tan color free of streaks. #1100 has special low density fillers incorporated into it that provide very distinct benefits. It is a very light material (4 pounds per gallon), and therefore contributes minimal added weight to the filled or repaired structure. Also, the cured material is very easy to sand, making the finished patch undetectable when covered or painted. There are no volatile ingredients in #1100, so the cured material will not outgas, which could cause a loss of adhesion of paint or coverings.#1100 is not corrosive to metals, and will not promote corrosion on these surfaces, so bond line stability and long term adhesion are excellent. #1100 is a non-toxic material. There are non hazardous or restricted raw materials in either the resin or hardener of this system.Information provided by Fibre Glast Developments Corporation.
Physical Properties Metric English Comments
Density 0.490 g/cc
0.0177 lb/in³
ASTM D1475
Water Absorption <= 0.40 %
<= 0.40 %
ASTM D570
Mechanical Properties Metric English Comments
Hardness, Shore D 53
53
Cured; ASTM D2240
Compressive Yield Strength 14.87 MPa
2156 psi
ASTM D695
Processing Properties Metric English Comments
Cure Time 120 - 180 min
2.00 - 3.00 hour
2 to 3 hours to shape at 77°F.
300 - 360 min
5.00 - 6.00 hour
5 to 6 hours to send at 77°F.
1440 min

@Temperature 25.0 °C,
Time 86400 sec
24.0 hour

@Temperature 77.0 °F,
Time 24.0 hour
24 hours to full cure at 77°F.
Pot Life 25 - 30 min
25 - 30 min
ASTM D2471
Gel Time 25.0 - 30.0 min
25.0 - 30.0 min
Value for 4 fl. oz.; ASTM D2471
Descriptive Properties Value Comments
Color Light Grayish-tan
Mix Ratio 100:50
Resin:Hardener by Weight
2:1
Resin:Hardener by Volume