Fibre Glast 2000 / 2020 System 2000 Epoxy

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler
Manufacturer Fibre Glast Developments Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fibre Glast 2000 / 2020 System 2000 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
System 2000 Epoxy Resin is a low viscosity, light amber laminating resin that is designed for fabricating parts and other demanding structural applications. Use this system to maximize the physical properties of carbon fiber, Kevlar®, and glass laminates! Test results have proven superiority over other room temperature epoxies. Its low viscosity and great handling characteristics make it a favorite in the shop too!Three high performance hardener systems are available for the System 2000 resin. 20 minute, 60 minute, and 120 minute pot life versions are all options. This added variety allows the fabricator to select the system best suited to the size, complexity or time-frame of the project. Simple parts which need to be demolded quickly should use the 20 minute hardener. Larger and more complex parts can use either of the other hardeners.Vacuum bagging applications would typically warrant the longest 2 hour working time. As with any epoxy system, adhere to the proper mix ratios and maintain an adequate curing temperature of at least 70°F. The cure time will be cut in half for every 10°F that the temperature is raised above 70°F.The short 20 minute pot life of the 2020 Epoxy Hardener is quite versatile. Use for repairs, simple fabrications, or those parts requiring a quick demold time.Information provided by Fibre Glast Developments Corporation.
Physical Properties Metric English Comments
Density 1.12 - 1.13 g/cc
0.0405 - 0.0408 lb/in³
Viscosity 950 - 975 cP
950 - 975 cP
ASTM D2293
Mechanical Properties Metric English Comments
Hardness, Shore D 88
88
Cured; ASTM D2240
Tensile Strength at Break 312.51 MPa
45326 psi
Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638
Elongation at Break 1.93 %
1.93 %
Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638
Tensile Modulus 17.4 GPa
2530 ksi
Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.
Flexural Strength 450.28 MPa
65308 psi
Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790
Flexural Modulus 19.5 GPa
2830 ksi
Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790
Thermal Properties Metric English Comments
CTE, linear 67.1 µm/m-°C

@Temperature 37.8 - 65.6 °C
37.3 µin/in-°F

@Temperature 100 - 150 °F
ASTM D696
Glass Transition Temp, Tg 82.2 °C
180 °F
Processing Properties Metric English Comments
Pot Life 20.0 min

@Temperature 25.0 °C
20.0 min

@Temperature 77.0 °F
4 fl. Oz.; ASTM D2471
Descriptive Properties Value Comments
Color Amber
Mix Ratio 100:23
Resin:Hardener by Weight
4.3:1
Resin:Hardener by Volume