Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. Film mechanical properties are comparable to premium strength LLDPE film resins. FormoleneFORMAX® L9 is formulated with slip and antiblock for use in high performance film applications offering excellent extrusion processing and outstanding impact strength and tear resistance. Films exhibit good optical properties. Formolene FORMAX® L9 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Industrial packaging, Industrial liners, Food packaging, Can liners, Consumer trash bags and CoextrusionInformation provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.915 g/cc
0.0331 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.51 MPa
1525 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.5 MPa
1530 psi
ASTM D882
Film Elongation at Break, MD 670 %
670 %
ASTM D882
Film Elongation at Break, TD 880 %
880 %
ASTM D882
Elmendorf Tear Strength MD 465 g
465 g
ASTM D1922
Elmendorf Tear Strength TD 650 g
650 g
ASTM D1922
Dart Drop Test 535 g
1.18 lb
ASTM D1709
Film Tensile Strength at Break, MD 39.3 MPa
5700 psi
ASTM D882
Film Tensile Strength at Break, TD 34.5 MPa
5000 psi
ASTM D882
Heat Seal Strength Initiation Temperature 103 °C

@Thickness 0.0508 mm
217 °F

@Thickness 0.00200 in
FPC
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 2.5
2.5