Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 45T Thin-Film TR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 73
73
60°C for 500 hrs; ASTM D2240
75
75
ASTM D2240
85
85
150°C for 1,000 hrs; ASTM D2240
87
87
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 5.11 MPa
741 psi
5.77 MPa
837 psi
150°C for 1,000 hrs
7.11 MPa
1030 psi
200°C for 1,000 hrs
Elongation at Yield 40 %
40 %
200°C for 1,000 hrs
60 %
60 %
150°C for 1,000 hrs
100 %
100 %
Tear Strength 0.400 kN/m
2.28 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 7.40e+13 ohm-cm
7.40e+13 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
6.50e+15 ohm-cm
6.50e+15 ohm-cm
150°C for 1,000 hrs
6.90e+15 ohm-cm
6.90e+15 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 4.4

@Frequency 1000 Hz
4.4

@Frequency 1000 Hz
After 1000 hrs at 150°C
4.4

@Frequency 50 Hz
4.4

@Frequency 50 Hz
After 1000 hrs at 150°C
4.4

@Frequency 1e+6 Hz
4.4

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
4.5

@Frequency 1e+6 Hz
4.5

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
4.5

@Frequency 50 Hz
4.5

@Frequency 50 Hz
After 1000 hrs at 200°C
4.5

@Frequency 1000 Hz
4.5

@Frequency 1000 Hz
After 1000 hrs at 200°C
4.9

@Frequency 1e+6 Hz
4.9

@Frequency 1e+6 Hz
After 500 hrs at 60°C
5.0

@Frequency 1000 Hz
5.0

@Frequency 1000 Hz
After 500 hrs at 60°C
5.2

@Frequency 50 Hz
5.2

@Frequency 50 Hz
After 500 hrs at 60°C
Dielectric Strength 7.00 kV/mm
178 kV/in
60°C for 500 hrs
10.0 kV/mm
254 kV/in
AC 60 Hz; 150°C for 1,000 hrs
10.0 kV/mm
254 kV/in
AC 60 Hz; 200°C for 1,000 hrs
11.0 kV/mm
279 kV/in
AC 60 Hz
Dielectric Breakdown 8000 V
8000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0020

@Frequency 50 Hz
0.0020

@Frequency 50 Hz
After 1000 hrs at 150°C
0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
After 1000 hrs at 150°C
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
After 1000 hrs at 200°C
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
0.0030

@Frequency 1e+6 Hz
0.0030

@Frequency 1e+6 Hz
0.0030

@Frequency 50 Hz
0.0030

@Frequency 50 Hz
After 1000 hrs at 200°C
0.0040

@Frequency 50 Hz
0.0040

@Frequency 50 Hz
0.0050

@Frequency 1e+6 Hz
0.0050

@Frequency 1e+6 Hz
After 500 hrs at 60°C
0.016

@Frequency 1000 Hz
0.016

@Frequency 1000 Hz
After 500 hrs at 60°C
0.039

@Frequency 50 Hz
0.039

@Frequency 50 Hz
After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Gray-Green
Thermal Impedance 0.73°C/W
FTM P-3010; ASTM D5470